| Grade | Structure | Styrene Content, %. |
300% Stretching Strength MPa |
Tensile Strength Mpa |
Elongation % |
Permanent Set % | Hardness Shore A | Toluene Solution Viscosity at 25℃, 25%,mpa.s |
| YH-501T | Linear | 30 | 5.0 | 20.0 | 490 | 24 | 76 | 600 |
| YH-502T | Linear | 30 | 4 | 27.0 | 540 | 16 | 73 | 180 |
| YH-503T | Linear | 33 | 6.0 | 25.0 | 480 | 16 | 74 | 2,300 |
| YH-604T | Radial | 33 | 5.8 | 30.0 | 530 | 20 | 78 | 2,200 |
| TSRC 6151 | Linear | 31-34 | - | - | - | - | - | 1700 |
| Grade | Structure | Styrene Content % |
Tensile Strength Mpa | Hardness Shore A | MFR (g/10min,200℃,5kg) |
Toluene Solution Viscosity at 25℃ and 25%,mpa.s |
| YH-188E | Linear | 32 | 26 | 85 | 6 | - |
| YH-791H | Linear | 28-32 | 20 | 76 | 0.1 | - |
| YH-815E (OE) | Radial | 40 | 24 | 89 | 0.1 | - |
| T-171E (OE) | Radial | 40 | 6 | 45 | 2-8 | - |
| Grade | Relative viscosity | Moisture w/% |
Relative Density | Melt Index g/10min |
Tensile Strength Mpa |
Elongation at break % |
| PA6 BL1340 | 3.3±0.05 | ≤0.06 | 1.12-1.15 | 5.7-6.8 | 65-75 | 100-160 |
| PA6 BL3200 | 2.05±0.05 | ≤0.06 | 1.12-1.15 | 160-200 | 55-65 | 10-20 |
| PA6 BL3240 | 2.45±0.05 | ≤0.06 | 1.12-1.15 | 30-45 | 55-65 | 30-50 |
| PA6 BL3280 | 2.78±0.05 | ≤0.06 | 1.12-1.15 | 30-45 | 55-65 | 30-50 |
| PA6 BL5400 | 4.00±0.10 | ≤0.06 | 1.12-1.15 | 2.3-2.8 | 65-75 | 150-300 |
| Grade | Tensile Strength | Tensile Strain at Break | Flexural Strength | Flexural Modulus | Izod Notched Impact Strength | Flow rate ratio |
| PA6 NCT02 | 50 | 40 | 65 | 1500 | 50 | 15 |
| Grade | Relative viscosity | Moisture w/% |
Relative Density | Melt Index g/10min |
Tensile Strength Mpa |
Elongation at break % |
| SL 803G |